    Plasma-induced graft polymerization on the surface of aramid fabrics with improved omniphobicity and washing durability

    2020-06-14 08:45:42EshragaSIDDIG尚曉冉YuXU徐雨TaoHE何濤MingGAO高明BaojingYANG楊寶敬TianshuWANG王天舒andJingZHANG張菁
    Plasma Science and Technology 2020年5期
    關(guān)鍵詞:高明

    Eshraga A A SIDDIG (尚曉冉),Yu XU (徐雨),Tao HE (何濤),Ming GAO (高明),Baojing YANG (楊寶敬),Tianshu WANG (王天舒) and Jing ZHANG (張菁),3,6

    1 New Energy Material and Device,College of Science,Donghua University,Shanghai 201620,People’s Republic of China

    2 College of Engineering,Sudan University of Science and Technology (SUST),Khartoum 11111,Sudan

    3 Magnetic Confinement Fusion Research Center,Ministry of Education,Shanghai 201620,People’s Republic of China

    4 Shenzhen Institutes of Advanced Technology,Chinese Academy of Sciences,Shenzhen 518055,People’s Republic of China

    5 Precision Chemical Technology (Shanghai) CO.,Ltd,Shanghai 201613,People’s Republic of China

    6 Authors to whom any correspondence should be addressed.

    Abstract

    Keywords:aramid fabrics,plasma-induced graft polymerization,hydrocarbon resistance,water repellency,washing durability

    1.Introduction

    Figure 1.The chemical structures of (a) aramid fabrics (poly-phenylene terephthalamide (PPTA)),(b) the monomer solution (polyperfluoralkyl methlacrylate copolymer emulsion,AG-E081).

    Aramid fabrics attracted researchers attention because of their high fraction point,high strain strength,excellent thermal stability,low density and fire resistance,which make them the first choice for the protective clothing of firefighters and in military applications [1].Highly hydrophobic and/or oleophobic surfaces are desirable for practical applications,including self-cleaning,non-fouling,stain-free clothing,protective clothing,drag reduction,corrosion prevention and the separation of liquids.Unfortunately,because of its compact molecule structure and smooth surface,it is relatively difficult to apply a hydrophobic coating to aramid fabric [2,3].Several techniques have been proposed,including C8 fluorine(perfluorinated compounds with 8 CF2groups),sol-gel or plasma polymerization [4–7].Generally,C8 fluorine and direct fluorination treatment are the main strategies,and can improve the omniphobicity and interfacial adhesion with little damage to the polymer [8,9].For instance,Jeong improved the hydrophobicity and oleophobicity of aramid fabric by direct fluorination [10].However,the reactions of polymers with F2are difficult to control due to the high reactivity of fluorine gases [11].The OEKO-TEX Standard 100 requires C8 to be replaced because it is persistently bio-accumulative and toxic for human beings.So,C6 fluorine,which causes fewer ecological and environmental problems,as well as nonfluorine hydrophobic agents,have been highly pursued in recent years—although the omniphobicity and durability of these methods are not as good as the C8 fluorine coating.

    Since hydrophobicity and/or oleophobicity is mainly related to the surface layer molecules,the plasma surface modification method can be efficiently tailored to increase the omniphobicity of fabrics[12].Abundant active species in the plasma can interact with the polymer surface and induce physical and chemical changes on the surface,and thus also improve the interfacial bonding and the adhesion properties[13,14].Previous studies have confirmed that the plasma process can prepare hydrophobic surfaces on conventional textile fabrics [15,16].Moreover,it has been shown that the procedure can be done in mild conditions.

    In contrast to the extensive studies on preparing omniphobic surfaces by plasma surface modification,the durability of the coating after washing has only been mentioned in a few pieces of research [17,18].It is well known that most textile fabrics undergo repeated laundering during their lifetime,therefore,the durability of fabric to laundry washing is significantly important [19].Taking into account the inert chemical surface and the low surface energy of the aramid fiber,the adhesion between the aramid fabric and the coating is poor,and thus the coating breaks away from the fabric during repeated washing—especially when C6 fluorine agents with short CF2chains are applied.Therefore,from the view of environmental requirements and commercial applications,it is necessary to study the C6 coating method and improve its omniphobicity and washing durability.

    In this work,superomniphobic aramid fabrics were prepared by the plasma-induced graft polymerization of a C6 fluorine emulsion solution in a two-step process.The surface morphology,surface chemical structure and composition of the fabric were investigated,and the hydrophobic and oleophobic performance of the as-prepared fabrics was evaluated by measuring the water contact angle and performing an AATCC spray test as well as a hydrocarbon resistance test.Moreover,the washing durability was further assessed and the mechanism was discussed.It is believed that the plasma process can lead to physical and chemical changes on the fabric surface,which is beneficial for improving its hydrophobic and oleophobic performance and washing durability.

    2.Experimental

    2.1.Materials

    Plain weave aramid poly-phenylene terephthalamide (PPTA)fabrics were used in this study.The fabrics were washed in distilled water for 30 min at 100°C and dried at 100°C for 1 h.The cleaned samples were chopped into dimensions of 25 cm × 25 cm for the experiment.Oxygen and argon(purity 99.99%) were bought from Shanghai Cheng Gong Gas Industry Co.,Ltd.The C6 fluorine emulsion solution was perfluoralkyl methlacrylate copolymer (AG-E081),which was provided by Precision Chemical Technology (Shanghai)Co.Ltd.The molecular structures of the aramid fabric and C6 fluorine are shown in figures 1(a) and (b).

    2.2.Plasma surface activation parameters

    A capacitor(AP-600/300TMNordson MARCH)coupled in a vacuum state was used for the surface treatment in this study,as shown in figure 2(a).An RF capacitively coupled plasma device powered at 13.56 MHz was used.The substrate is placed downstream of the chamber between the two parallel shelf electrodes with a 2 inch gap.The plasma system was evacuated first for 10 min to reach a lower pressure(≤20 mTorr),and then a mixture of Ar/O2gases with a flow rate ratio of 10:90 sccm filled the reaction chamber,which increased the vacuum base pressure to about 250 mTorr.The increased amount of O2was a good choice for improving the surface properties (such as wettability and adhesion) with very low degradation levels;as for Ar only a small amount is needed for the cleaning process.During the treatment process,the power was set as 300 W and the treatment duration was set as 300 s.This end is consistent with experimental work after optimizing the discharge conditions for our material.

    The radicals and ions in the reactive plasmas were diagnosed by optical emission spectroscopy (OES) in the visible and near infrared regions.The OES spectrum is shown in figure 2(b).The oxide O-negative ions are created in the bulk of plasma.The significant lines for the experimental conditions are 777.2 nm and 844.6 nm [20].

    Figure 2.(a) A schematic diagram of the plasma setup,(b) the optical emission spectra from the Ar/O2 discharge.

    Table 1.The final aramid sample names.

    2.3.Fluorination of the aramid fabric

    The aramid fabrics were immersed in aqueous solutions of poly-perfluoralkyl methlacrylate copolymer emulsion,AGE081 (30%,w/w) at room temperature,then padded and dried at 170°C for 2 min.After that,all samples were rinsed with distilled water to eliminate the residual chemicals before tests.The final aramid fabrics are referred to as sample P,sample F and sample PF,according to whether the fabric had been subjected to plasma treatment,the fluorine coating or both,as shown in table 1.The control is referred to as sample C in the following discussion.

    2.4.Washing durability test

    The washing durability was investigated by subjecting sample F and sample PF to ten washing cycles,which are then referred to as sample FW1,sample FW5,sample FW10and sample PFW1,sample PFW5,sample PFW10,as shown in table 1.Each washing cycle was carried out with standard soap (11 g) for 1 h followed by drying in a microwave at 60°C for 1 h.An AATCC spray test,a hydrocarbon resistance test as well as some other characterization tests were carried out before and after the washing cycles.

    2.5.Fabric surface characterization

    A field emission scanning electron microscope (FE-SEM,S-4800,Hitachi,Japan) was used to observe the surface morphologies of the aramid fabrics.Before the observation,the samples were coated with a thin gold layer of less than 100 ? to prevent charging on the surface of the fabrics.

    ATR-FTIR spectrophotometer attenuated total reflection(Nicolet 6700,Thermo Fisher,USA)was used to analyze the chemical structure of the aramid fabric surface.The FTIR spectra were recorded in the range 500–4000 cm-1at a resolution of 4 cm-1.

    The surface chemical compositions of the aramid fabrics were investigated using a Kratos Axis Ultra DLD x-ray photoelectron spectroscope (Shimadzu,Japan)equipped with an Al K source.The base pressure in the analysis chamber was less than 5 × 10–9Torr and the spectra were acquired at a take-off angle of 90°.The binding energy (BE) scale was calibrated according to the C1s peak (284.8 eV) of adventitious carbon on the analyzed fabric surface.Deconvolution analysis of the C1s and O1s peaks was carried out using XPS peak analysis software.

    2.6.Water and oil repellency testing

    The water contact angles were measured using a drop meter A-200 computer-video-processed goniometer (MALSI,China).The data was read at three different points on each sample,and the averages with standard deviation were calculated.

    A homemade right-angle triangle method was employed to test the rolling angles with a 2.9°angle and droplet size of less than 0.03 ml.

    For textile fabric in practical application,the resistance of the fabrics to wetting with water was measured by the AATCC spray test method.After the spray test,the wet faces of the different types of aramid fabrics were rated according to the AATCC photographic standards.

    Figure 3.SEM images of aramid fabrics:(a)sample C,(b)sample F,(c)sample FW10,(d)sample P,(e)sample PF,and(f)sample PFW10.

    An AATCC hydrocarbon resistance test was carried out to evaluate the resistance of the aramid fabrics to oil stains.A series of four liquid hydrocarbons,including n-tetradecane(grade number 4),n-dodecane (grade number 5),n-decane(grade number 6) and n-oclane (grade number 7) with different surface tensions of 26.4 mN m-1,24.7 mN m-1,23.5 mN m-1and 21.4 mN m-1respectively,were selected for the test.Drops of the standard test liquids were placed on the fabric surface and observed for wetting,wicking and contact angle,with the following results:A=passes with a clear well rounded drop;B=borderline passes with a rounding drop and partial darkening;C=fails with wicking apparent and/or complete wetting and D=fails with complete wetting.The AATCC oil repellency grade is the highest numbered test liquid which does not wet the fabric surface,within a period of 30 ± 2 s.

    3.Results and discussions

    3.1.Surface morphology

    The surface morphology of the aramid fabrics was investigated using SEM,and the images are shown in figure 3.It can be seen from figure 3(a) that the untreated aramid fabric sample C presents a relatively smooth surface.When the untreated fabric was coated directly with AG-E081 emulsion(sample F),only partially covered protrusion shapes appeared in the fabric surface,as shown in figure 3(b),suggesting that some of the fluorine coating had not adhered so closely.Because of the inert chemical properties and smooth surface of the aramid fabrics,the fluorine coating seriously flaked off following ten washing cycles (sample FW10) as seen clearly in figure 3(c).

    After plasma treatment,it can be obviously seen that the fabric surface of sample P has become rough and uneven.As presented in figure 3(d),a lot of apparent bulges and ruts can be observed[21].The changes in surface morphology can be attributed to the physical and chemical etching effect caused by active particles in the plasma [22].It is supposed that a rough morphology will be beneficial for the adhesion of the C6 fluorine copolymer [23].After further plasma graft polymerization with the C6 fluorine coating (sample PF),a homogenous layer of C6 fluorine copolymer can be seen,as shown in figure 3(e),indicating that the fiber surface was completely covered with the fluorine copolymer.After ten washes (sample PFW10),the coating was largely preserved and only slight morphology changes were observed as shown in figure 3(f).These results imply that the adhesion of the coating to the fabric was enhanced by plasma pre-treatment.

    3.2.Surface chemical structure

    ATR-FTIR analysis was used to characterize the chemical structure of the samples,which can confirm the bonding status of the C6 fluorine copolymer onto the aramid fabric.The typical characteristic peaks of the controlled aramid sample are assigned to the C–H/C–N aromatic ring at 853 cm-1,C–O–C stretching at 1083 cm-1and C–H stretching (amide III) at 1240 cm-1;further the C=O stretching in primary amide I at 1643 cm-1and 3292 cm-1is owing to the N–H stretch in the amide terminal (alkynes)[24–26].

    Figure 4.The FTIR spectrum of aramid fabrics.(a)Sample C and sample P:storage in air after plasma treatment for 5 h,1 day and 5 days,(b) sample F and sample PF,(c) sample FW10 and sample PFW10.

    Table 2.The surface elements of the aramid samples by XPS.

    From figure 4(a),the spectrum profiles of the plasmatreated aramid fabrics (sample P,5 h,1 day and 5 days) are not significantly different from the control sample C.However,a difference is noticed for peaks at 1740 cm-1and 1083 cm-1.For sample 5 H(storage in air for 5 h after plasma treatment),a shoulder peak appeared at 1740 cm-1and the intensity at 1740 cm-1increased with the storage time.For samples 1 D and 5 D(storage in air for 1 or 5 days),the peak at 1740 cm-1was obvious.The intensity at 1083 cm-1also increased with the storage time.As will be discussed later in figure 7,this is attributed to the reaction of the active surface with the storage conditions,leading to the introduction of polar groups,such as the COOH group.

    In figure 4(b),the intensity of the peak at 1240 cm-1increased significantly for sample PF and sample F compared with sample P.It should be noted that C–F stretching in the aliphatic fluoro-compounds was observed in the range of 1000–1300 cm-1.Thus,this increased peak intensity may indicate that the C6 fluorine copolymer had attached to the fabric surface [27].In addition,there was a new strong absorption peak at 1740 cm-1and its intensity was greater for sample PF than for sample F,which is attributed to the ester groups on the alkyl methlacrylate graft chain [28].This also confirmed the presence of the C–F functional C6 fluorine copolymer on the fabric surface.

    As displayed in figure 4(c),after ten washing cycles,the relative intensity of the characteristic peaks of the C6 copolymer at 1740 cm-1and 1240 cm-1decreased,which indicates a decreased amount of the coating after washing.It is also indicates that the relative intensity of the peaks at 1740 cm-1and 1240 cm-1decreased more for sample FW10than for sample PFW10,which shows that the plasma treatment enhanced the tolerance of the C6 copolymer coating to washing.The results indicate that the C6 fluorine functional groups have been introduced into the surface of the aramid fabric after coating,and the plasma treatment facilitated better grafting of the C6 fluorine molecules into the aramid fabric through the introduction of polar groups like COOH.

    3.3.Surface chemical composition

    The surface chemical compositions of the aramid fabrics were investigated by XPS.Table 2 shows the bond percentages of the surface elements and their relative ratio to carbon.Compared to sample C,the [O]/[C]ratio of sample P increased markedly upon increasing the oxygen concentration.This indicates that new oxygen containing groups had been incorporated into the fabric surfaces,corresponding well with the bond percentage shown in figure 5 and the FTIR results.In comparison with sample C and sample P,the atomic ratio of [F]/[C]of the coated samples (sample F and sample PF)with C6 fluorine increased greatly and this ratio increased most for sample PF.After repeated washing cycles,the[F]/[C]ratio decreased for all the C6 fluorine coated samples.Moreover,the [F]/[C]ratio decreased less for the plasma-treated and coated samples(sample PFW1and sample PFW10)than for only the C6 fluorine coated samples(sample FW1and sample FW10).This result indicates that plasma treatment activated the aramid surface and enhanced the graft polymerization of the active aramid molecules with the C6 fluorine copolymers.

    Figure 5.The deconvoluted XPS C1s of the aramid fabrics.(a)Sample C,(b)sample F,(c)sample FW10,(d)sample P,(e)sample PF and(f) sample PFW10.

    Deconvolution analysis of the C1s peaks was performed,see figure 5.As shown in figure 5(a)for sample C,there were four kinds of carbon states:C–C at 284.8 eV,C–N/C–O at 285.6 eV,CO–NH at 286.9 eV and CO–OH at 288.5 eV[29].As indicated in figure 5(d) for sample P,the relative intensities of the peaks of CO–OH to C–C increased a lot after plasma treatment due to the broken bonds C–C/C–H and the recombination of oxygen atoms,suggesting that new oxygencontained functional groups C–O,C=O or COOH had been formed [30].Furthermore,the component due to the π–π*shake-up satellite indicated some instauration of the active surface in the plasma polymer [31,32].

    After fluorination,three new peaks at 289 eV,291.9 eV and 293.9 eV were observed—see figures 5(b) and (e)—corresponding to C=O,CF2and CF3respectively [33,34].Compared to the directly fluorine-coated sample F in figure 5(b),the relative peak intensity of CF2and CF3in sample PF in figure 5(e) increased significantly,indicating that more fluorine polymer had been introduced into the fabric surface.Moreover,it can also be seen from figure 5(c)that the peak intensities of CF2and CF3are lower after washing for sample FW10than for PFW10.On the basis of this,the washing repellency of the C6 fluorine coating for sample PF is more durable.

    3.4.Water and oil repellency performance

    It is well known that fluorine functional groups are beneficial to the hydrophobic performance of the surface.The extent of hydrophobic modification of the aramid fabric was studied with a static water contact angle measurement after repeat washing cycles,as shown in figure 6(a).It can be seen that the contact angle value of the direct fluorine coated sample F before washing was 174°.The contact angle declined from 155.1°for one wash to 134°for five washes and 104°for ten(knowing that the sample C contact angle was 99.1°).With a fluorine graft coating,a remarkable increase in contact angle can be seen in figure 6(a).Sample PF exhibited good hydrophobicity with the water contact angle 179.9°.After repeated wash cycles from one,to five and ten,the water contact angles were almost stable at 179.8°,179.7°and 179°,respectively,while the rolling angles were assumed to be less than 2°.Generally,superhydrophobic surfaces exhibit roll-off angles less than 5°,and very specific surfaces can exhibit rolloff angles of less than 1° [35].The rough surface and large amount of reactive radicals that formed on sample PF improved the absorption and reaction of the fluorine molecules on the fabric surface.Further,fluorine molecules graft well compared to sample F,which had a smooth surface with a droopily fluorine coating pointing to a decrease of the contact angle.This means that a durable super hydrophobic surface had formed on the plasma-treated aramid fabrics.

    Figure 6.(a) The water contact angle versus washing cycles and (b) water spray standard test (AATCC) photographs after repeat washing cycles from 0,1,5 to 10 respectively on aramid fabrics.(a) Sample F,(b) sample FW1,(c) sample FW5,(d) sample FW10,(e) sample PF,(f) sample PFW1,(f) sample PFW5 and (f) sample PFW10, respectively.

    Table 3.Water spray standard test and standard oil test of aramid samples.

    To evaluate the water and oil repellent properties in a practical way,a spray test and hydrocarbon resistance test were carried out according to the AATCC standard.As depicted in table 3,sample C showed a spray rating of 50,indicating that the aramid fabric had poor surface hydrophobicity.After plasma treatment,a zero spray rating was obtained for sample P,implying that the fabric is hydrophilic by the plasma modification.Compared with sample C and sample P,sample F and sample PF exhibited a spray rating above 90 after fluorine coating,indicating good water repellency.In addition,sample PF showed a higher spray rating(100) than sample F (90).

    For oil repellency,both sample C and sample P showed an oil repellency of D in grade number 4,suggesting that they have poor oil repellency.After fluorine coating,sample F had oil repellency A in grade number 4 and D in grade number 6,indicating good oil repellency gained from the fluorine functional groups.Moreover,sample PF obtained higher oil repellency grades (D in grade number 7) than the other samples,which exhibited the best oil repellency.These results demonstrated that the effectiveness of the introduced fluorine functional groups was enhanced by plasma treatment.

    Table 4 summarizes the oil and water repellent durability of the samples after different washing cycles.It can be seen that after one cycle of washing,sample FW1has a B in grade number 4 and C in grade number 5,which shows a decrease compared to sample F.Interestingly,there were no differences in the grades of sample PF W1after washing.After five wash cycles,the oil repellency of sample FW5was not oleophobic in grade number 5.In contrast,sample PFW5remained unchanged in grade numbers 4 and 5,and showed a fail in grade number 6.After ten washing cycles,sample F had no oil repellency,while sample PF still showed an oil repellency of B in grade number 4 and C in grade number 5.

    For water repellency durability,the results were consistent with the oil repellency behavior.After one cycle,the spray rating values of sample FW1decreased to 70,while the values remained unchanged for sample PFW1.After five wash cycles,a further decrease of the spray rating values was observed in sample FW5,and only a few changes appeared in sample PFW5.After ten wash cycles,sample FW10showed a disappointing result with a spray rating of 0.Fortunately,the spray rating of sample PF W10remained at 80,which indicates the good durability of the fluorine coating on the aramid fabric achieved by the plasma process.

    As shown above,the plasma treatment changed the surface roughness,activated the aramid molecules and introduced oxygen polar groups on the aramid fabric surfaces,by breaking the pi (π),sigma (σ) and delta (δ) bonds at several places on the polymer chains via a free radical initiation.

    Figure 7 depicts the fabrication process and the suggested mechanism only breaking the bond at –CO–NH–.The active species of high-energy electrons and ions in plasma can lead to polymer chain scissions,which will create a rough surface and a large amount of reactive radicals.Rough and reactive radicals will react with the circumstance particles and form oxygen-containing functional groups as displayed in FTIR and XPS spectra,becoming reactive and attractive to the thermal dissociated opened C=C bonds in fluorine molecules.This will further improve the absorption and reaction of the fluorine molecules on the fabric surface.Further,fluorine molecules get into the rough surface and then the graft polymerization with opened C=C bonds.Therefore,durable hydrophobic and oleophobic surfaces are obtained.

    Table 4.Water spray standard test and standard oil test after repeating washing cycles of aramid samples.

    Figure 7.Schematic diagrams for the mechanism of preparing durable omniphobic aramid fabric.

    4.Conclusions

    In summary,in order to prepare a durable omniphobic aramid surface,the plasma-induced graft polymerization of C6 fluorine copolymer was utilized.Durable superomniphobic surfaces are desirable for practical applications,including self-cleaning,non-fouling,stain-free clothing,drag reduction,corrosion prevention,separation of liquids,for use in protective clothing for firefighters and military applications.After the process,the as-prepared fabrics became super-hydrophobic with a water contact angle of 180°and are kept stable after ten washes.Through the AATCC spray test and hydrocarbon resistance test,the modified fabrics can achieve a B in grade number 6 for oil repellency and a spray rating of 100°(ISO 5)for water repellency.The results of the AATCC spray test and hydrocarbon resistance test also showed good durability after ten washes.The omniphobicity and washing durability can be attributed to abundant active species introduced by the plasma treatment and the effectiveness of the graft C6 fluorine copolymer in the structure of the aramid fabrics,which improved the omniphobicity and washing durability.This study demonstrates that the plasma-induced graft polymerization process is a promising alternative for superomniphobic surface modification with improved washing durability when replacing C8 with C6 fluorine copolymers.

    Acknowledgments

    This work was supported by the Fundamental Research Funds for the Central Universities 2232019A3-12 and National Natural Science Foundation of China (No.11375042).

    猜你喜歡
    高明
    Propagation of surface magnetoplasmon polaritons in a symmetric waveguide with two-dimensional electron gas
    FeS介導(dǎo)下的1,2-二溴乙烷非生物自然衰減
    明明家族歷險(xiǎn)記
    ——辨析聰明、精明、高明、英明
    Heredity of clusters in the rapidly cooling processes of Al-doped Zr50Cu50 melts and its correlation with the glass-forming ability*
    Enhanced electrocatalytic activity of carbon cloth by synergetic effect of plasma and acid treatment
    《實(shí)數(shù)》典型易錯(cuò)題
    爸爸的“高明”之處
    Study on the Perturbation Characteristics of Two-Channel Laser Propagation in Atmospheric Turbulence
    聰明人,精明人,高明人
    看走眼了
    亚洲一码二码三码区别大吗| 色94色欧美一区二区| h视频一区二区三区| 国产野战对白在线观看| 精品国产超薄肉色丝袜足j| 国产精品久久久久久精品电影小说| 亚洲欧美一区二区三区久久| 久久精品久久精品一区二区三区| 激情五月婷婷亚洲| 成人国语在线视频| 久久久精品国产亚洲av高清涩受| 亚洲人成电影观看| 国产福利在线免费观看视频| 色94色欧美一区二区| 日本黄色日本黄色录像| 久久婷婷青草| 亚洲国产看品久久| 国产深夜福利视频在线观看| 国产精品久久久久久久久免| 少妇 在线观看| 日日爽夜夜爽网站| 十分钟在线观看高清视频www| 久久久久久久久久久免费av| 久久精品国产亚洲av涩爱| 国产伦理片在线播放av一区| 久久久精品免费免费高清| 国产亚洲精品第一综合不卡| 极品少妇高潮喷水抽搐| 三上悠亚av全集在线观看| 天堂俺去俺来也www色官网| 99久国产av精品国产电影| 最近手机中文字幕大全| 99久久99久久久精品蜜桃| 中文字幕高清在线视频| 啦啦啦在线免费观看视频4| 成人影院久久| av天堂久久9| 亚洲国产精品一区三区| 久久ye,这里只有精品| 大码成人一级视频| 中文精品一卡2卡3卡4更新| 国产精品亚洲av一区麻豆 | 国产免费一区二区三区四区乱码| 国产99久久九九免费精品| 夫妻午夜视频| 七月丁香在线播放| 亚洲国产av新网站| 亚洲av成人精品一二三区| 欧美日韩福利视频一区二区| 日韩伦理黄色片| 国产国语露脸激情在线看| 亚洲熟女精品中文字幕| 18在线观看网站| 91aial.com中文字幕在线观看| 亚洲精品自拍成人| 亚洲av欧美aⅴ国产| 中文字幕另类日韩欧美亚洲嫩草| 精品国产乱码久久久久久男人| 免费高清在线观看日韩| 黑丝袜美女国产一区| 色94色欧美一区二区| 美女脱内裤让男人舔精品视频| 国产成人精品在线电影| 亚洲中文av在线| 国产探花极品一区二区| 免费在线观看完整版高清| 亚洲成av片中文字幕在线观看| 久久久久精品人妻al黑| 日本黄色日本黄色录像| 男女床上黄色一级片免费看| 宅男免费午夜| 免费在线观看完整版高清| 99国产精品免费福利视频| 热99久久久久精品小说推荐| 亚洲视频免费观看视频| 亚洲视频免费观看视频| 亚洲,欧美,日韩| 成年人免费黄色播放视频| 啦啦啦 在线观看视频| 亚洲在久久综合| 国产探花极品一区二区| 欧美激情极品国产一区二区三区| 九草在线视频观看| 国产男女超爽视频在线观看| 亚洲成人av在线免费| 欧美日韩综合久久久久久| 久久精品人人爽人人爽视色| 国产熟女欧美一区二区| 国产免费福利视频在线观看| 日韩一本色道免费dvd| 这个男人来自地球电影免费观看 | 91精品国产国语对白视频| 色播在线永久视频| 亚洲精品国产av成人精品| 午夜91福利影院| 欧美人与性动交α欧美软件| 久久久久精品性色| 日韩免费高清中文字幕av| 午夜福利视频精品| 美女福利国产在线| 王馨瑶露胸无遮挡在线观看| 日本欧美国产在线视频| 日韩欧美精品免费久久| 精品久久久精品久久久| 国产精品99久久99久久久不卡 | 亚洲欧美一区二区三区黑人| 天堂中文最新版在线下载| 一级,二级,三级黄色视频| 欧美日韩视频精品一区| 午夜av观看不卡| 免费观看a级毛片全部| 美女主播在线视频| 日本wwww免费看| 亚洲免费av在线视频| 亚洲国产欧美在线一区| 2018国产大陆天天弄谢| 男女高潮啪啪啪动态图| 久久久久人妻精品一区果冻| 色播在线永久视频| 国产精品久久久久久精品电影小说| 亚洲欧美精品综合一区二区三区| 黄网站色视频无遮挡免费观看| 国产乱来视频区| 久久久久精品性色| 女的被弄到高潮叫床怎么办| 女人高潮潮喷娇喘18禁视频| 久久久精品免费免费高清| 亚洲欧美成人精品一区二区| 女人久久www免费人成看片| 亚洲第一区二区三区不卡| 老鸭窝网址在线观看| 亚洲熟女精品中文字幕| e午夜精品久久久久久久| 大码成人一级视频| 亚洲精品国产色婷婷电影| 精品少妇久久久久久888优播| 中文字幕av电影在线播放| 亚洲综合精品二区| 亚洲精品日本国产第一区| 国产精品99久久99久久久不卡 | 成人免费观看视频高清| 男女之事视频高清在线观看 | 午夜福利视频在线观看免费| 久久精品熟女亚洲av麻豆精品| 不卡av一区二区三区| 中文字幕亚洲精品专区| 国产亚洲精品第一综合不卡| 久久毛片免费看一区二区三区| 国产在线视频一区二区| 国产男女超爽视频在线观看| 精品免费久久久久久久清纯 | 国语对白做爰xxxⅹ性视频网站| netflix在线观看网站| 亚洲国产精品成人久久小说| 国产乱来视频区| 老熟女久久久| 秋霞伦理黄片| 亚洲久久久国产精品| 夫妻性生交免费视频一级片| 一级毛片黄色毛片免费观看视频| 亚洲激情五月婷婷啪啪| 亚洲天堂av无毛| 性少妇av在线| 亚洲成国产人片在线观看| 一级毛片电影观看| 看免费av毛片| 国产精品99久久99久久久不卡 | 纵有疾风起免费观看全集完整版| 日本av免费视频播放| 日韩一本色道免费dvd| 午夜老司机福利片| 日韩av免费高清视频| 丰满迷人的少妇在线观看| 天天躁日日躁夜夜躁夜夜| 久久久久网色| 久久久久久人人人人人| 亚洲美女搞黄在线观看| 久久久精品免费免费高清| 看免费成人av毛片| 叶爱在线成人免费视频播放| 满18在线观看网站| 一级片免费观看大全| 亚洲美女黄色视频免费看| 色吧在线观看| 久久久久精品国产欧美久久久 | 老汉色∧v一级毛片| 国产深夜福利视频在线观看| 国产xxxxx性猛交| 国产不卡av网站在线观看| 亚洲成色77777| 汤姆久久久久久久影院中文字幕| 操美女的视频在线观看| 一级毛片电影观看| 女人爽到高潮嗷嗷叫在线视频| 国产亚洲av高清不卡| 韩国精品一区二区三区| 亚洲视频免费观看视频| 精品国产露脸久久av麻豆| 亚洲人成电影观看| 亚洲精品乱久久久久久| av在线播放精品| 国产一区二区 视频在线| 国产99久久九九免费精品| 久久久久网色| 亚洲国产成人一精品久久久| 美女扒开内裤让男人捅视频| 国产av国产精品国产| av不卡在线播放| 激情视频va一区二区三区| 免费黄频网站在线观看国产| 精品一品国产午夜福利视频| 国产欧美亚洲国产| 欧美在线一区亚洲| 午夜老司机福利片| 午夜免费鲁丝| 丝袜脚勾引网站| 天天躁夜夜躁狠狠躁躁| 成人午夜精彩视频在线观看| 美女高潮到喷水免费观看| 母亲3免费完整高清在线观看| 久久久精品国产亚洲av高清涩受| 国产人伦9x9x在线观看| 老司机亚洲免费影院| 如何舔出高潮| 国产午夜精品一二区理论片| 一级毛片黄色毛片免费观看视频| 国产熟女午夜一区二区三区| 久久久精品94久久精品| 久久精品亚洲熟妇少妇任你| 在线亚洲精品国产二区图片欧美| 精品国产一区二区三区四区第35| 99国产精品免费福利视频| 人成视频在线观看免费观看| 免费不卡黄色视频| 国产亚洲最大av| 免费在线观看视频国产中文字幕亚洲 | 乱人伦中国视频| 人妻一区二区av| 51午夜福利影视在线观看| 观看av在线不卡| 成人18禁高潮啪啪吃奶动态图| 高清欧美精品videossex| 嫩草影视91久久| 欧美黑人欧美精品刺激| 日韩一本色道免费dvd| 爱豆传媒免费全集在线观看| 黄色毛片三级朝国网站| 丰满迷人的少妇在线观看| 中文字幕亚洲精品专区| 男女床上黄色一级片免费看| 男女边摸边吃奶| 亚洲成国产人片在线观看| 精品少妇内射三级| 一级a爱视频在线免费观看| 新久久久久国产一级毛片| 久久鲁丝午夜福利片| 最新的欧美精品一区二区| 久久久久视频综合| 午夜日韩欧美国产| 久久久久久久大尺度免费视频| 午夜福利一区二区在线看| 免费观看av网站的网址| 又大又黄又爽视频免费| 校园人妻丝袜中文字幕| 亚洲欧美激情在线| 日韩精品免费视频一区二区三区| av有码第一页| 少妇被粗大猛烈的视频| 国产精品免费大片| 超碰成人久久| 国产亚洲av片在线观看秒播厂| 成人免费观看视频高清| 欧美人与性动交α欧美精品济南到| 久久午夜综合久久蜜桃| 97人妻天天添夜夜摸| 国产色婷婷99| 大陆偷拍与自拍| 国产熟女午夜一区二区三区| 9色porny在线观看| 国产亚洲av高清不卡| 亚洲精品久久成人aⅴ小说| 免费观看人在逋| 日韩一卡2卡3卡4卡2021年| 午夜日韩欧美国产| 天堂俺去俺来也www色官网| 在线观看免费视频网站a站| 欧美激情高清一区二区三区 | 黄色 视频免费看| 欧美激情 高清一区二区三区| 超色免费av| 国产精品女同一区二区软件| 天堂俺去俺来也www色官网| a级片在线免费高清观看视频| 母亲3免费完整高清在线观看| 国产男人的电影天堂91| 日韩欧美精品免费久久| 晚上一个人看的免费电影| 99国产精品免费福利视频| 日韩av在线免费看完整版不卡| 国产精品欧美亚洲77777| 不卡av一区二区三区| 日韩一区二区视频免费看| 久久国产精品大桥未久av| 国产国语露脸激情在线看| 久久青草综合色| 韩国高清视频一区二区三区| 国产不卡av网站在线观看| 亚洲人成电影观看| 久久影院123| 一边摸一边做爽爽视频免费| 国产xxxxx性猛交| 精品免费久久久久久久清纯 | 女人高潮潮喷娇喘18禁视频| 国产精品.久久久| 久久精品亚洲av国产电影网| 国产人伦9x9x在线观看| 九色亚洲精品在线播放| 国产av一区二区精品久久| 久久免费观看电影| 国产成人啪精品午夜网站| 亚洲欧美中文字幕日韩二区| 精品一品国产午夜福利视频| 天天躁夜夜躁狠狠久久av| 大码成人一级视频| 亚洲自偷自拍图片 自拍| 在线观看人妻少妇| 最近中文字幕2019免费版| 日本一区二区免费在线视频| 91精品国产国语对白视频| 亚洲精品一区蜜桃| 亚洲第一区二区三区不卡| 色综合欧美亚洲国产小说| 热99国产精品久久久久久7| 日韩电影二区| 日韩av在线免费看完整版不卡| √禁漫天堂资源中文www| 午夜激情av网站| 久久精品aⅴ一区二区三区四区| 天天躁夜夜躁狠狠久久av| 国产视频首页在线观看| 精品国产超薄肉色丝袜足j| 久久鲁丝午夜福利片| 日韩精品有码人妻一区| 热re99久久国产66热| 极品少妇高潮喷水抽搐| 欧美日韩一区二区视频在线观看视频在线| 午夜激情久久久久久久| 曰老女人黄片| 欧美老熟妇乱子伦牲交| 制服诱惑二区| 亚洲精品久久午夜乱码| 国产欧美日韩一区二区三区在线| 亚洲av电影在线进入| 亚洲成国产人片在线观看| 一边摸一边抽搐一进一出视频| 考比视频在线观看| 91aial.com中文字幕在线观看| 啦啦啦在线免费观看视频4| 国产欧美日韩一区二区三区在线| 女性生殖器流出的白浆| 99热网站在线观看| www日本在线高清视频| 两个人免费观看高清视频| 这个男人来自地球电影免费观看 | 日韩一区二区视频免费看| 亚洲精品,欧美精品| 久久精品久久精品一区二区三区| av线在线观看网站| 亚洲欧美一区二区三区黑人| 亚洲国产中文字幕在线视频| 亚洲精品第二区| 亚洲,欧美,日韩| 别揉我奶头~嗯~啊~动态视频 | 国产探花极品一区二区| 少妇被粗大猛烈的视频| 王馨瑶露胸无遮挡在线观看| 国产又爽黄色视频| 天天操日日干夜夜撸| 欧美少妇被猛烈插入视频| 国产乱来视频区| 精品少妇黑人巨大在线播放| 日韩精品有码人妻一区| 亚洲欧美清纯卡通| 一区二区日韩欧美中文字幕| 天天躁夜夜躁狠狠久久av| 国产成人av激情在线播放| 国产成人欧美| 国产高清不卡午夜福利| 在线观看三级黄色| 街头女战士在线观看网站| 国产成人a∨麻豆精品| 亚洲国产毛片av蜜桃av| 永久免费av网站大全| 激情五月婷婷亚洲| 久久久久久免费高清国产稀缺| 90打野战视频偷拍视频| 成人国产av品久久久| 久久久久精品久久久久真实原创| 国精品久久久久久国模美| 黑人巨大精品欧美一区二区蜜桃| 久久人妻熟女aⅴ| 啦啦啦在线观看免费高清www| 国产精品一区二区精品视频观看| 国产一区二区三区综合在线观看| 日韩一卡2卡3卡4卡2021年| 9热在线视频观看99| 深夜精品福利| 国产黄频视频在线观看| netflix在线观看网站| 精品亚洲成a人片在线观看| 一级,二级,三级黄色视频| 啦啦啦在线免费观看视频4| 搡老岳熟女国产| 国产黄频视频在线观看| 久久精品国产综合久久久| 日韩欧美一区视频在线观看| 街头女战士在线观看网站| 色播在线永久视频| 久热这里只有精品99| 少妇人妻 视频| 成年人午夜在线观看视频| 九草在线视频观看| 又粗又硬又长又爽又黄的视频| 麻豆精品久久久久久蜜桃| 欧美日本中文国产一区发布| 一区二区三区精品91| 美女福利国产在线| av视频免费观看在线观看| 别揉我奶头~嗯~啊~动态视频 | 国产黄频视频在线观看| 久久久久精品国产欧美久久久 | 亚洲在久久综合| 成人国语在线视频| 超碰97精品在线观看| 亚洲人成77777在线视频| 欧美另类一区| 十八禁高潮呻吟视频| 久久99精品国语久久久| 日韩免费高清中文字幕av| kizo精华| 亚洲国产欧美在线一区| 国产无遮挡羞羞视频在线观看| 成年美女黄网站色视频大全免费| 黄片播放在线免费| 十八禁高潮呻吟视频| 在线观看免费日韩欧美大片| 亚洲精品国产av成人精品| 亚洲精品一二三| 一本色道久久久久久精品综合| 国产老妇伦熟女老妇高清| 成人午夜精彩视频在线观看| 日韩不卡一区二区三区视频在线| 天天躁日日躁夜夜躁夜夜| 午夜福利,免费看| 精品午夜福利在线看| 青春草国产在线视频| 亚洲欧美精品自产自拍| av国产精品久久久久影院| 在线观看免费视频网站a站| 日韩精品有码人妻一区| 水蜜桃什么品种好| 色网站视频免费| 国产视频首页在线观看| 丁香六月天网| 波多野结衣一区麻豆| 在线 av 中文字幕| 美女高潮到喷水免费观看| 午夜久久久在线观看| 十八禁高潮呻吟视频| 欧美日韩成人在线一区二区| 午夜福利影视在线免费观看| 国产一区二区三区综合在线观看| xxx大片免费视频| 嫩草影视91久久| 亚洲美女黄色视频免费看| 国产老妇伦熟女老妇高清| av有码第一页| 制服人妻中文乱码| 精品一区二区三卡| 又大又黄又爽视频免费| 麻豆精品久久久久久蜜桃| 免费女性裸体啪啪无遮挡网站| 啦啦啦在线免费观看视频4| 考比视频在线观看| 国产成人91sexporn| 亚洲av综合色区一区| 亚洲av欧美aⅴ国产| 亚洲国产最新在线播放| 国产成人一区二区在线| 国产精品免费大片| 国产在线一区二区三区精| 欧美日韩视频精品一区| 欧美日韩精品网址| 香蕉丝袜av| 国产av国产精品国产| 国产不卡av网站在线观看| 大码成人一级视频| 韩国精品一区二区三区| 国产黄频视频在线观看| 男人爽女人下面视频在线观看| 夫妻性生交免费视频一级片| 人人澡人人妻人| 男女无遮挡免费网站观看| 七月丁香在线播放| 久久久久久人人人人人| 亚洲精品自拍成人| 亚洲美女搞黄在线观看| 国产黄色免费在线视频| 国产精品嫩草影院av在线观看| 看十八女毛片水多多多| 国产成人av激情在线播放| 国产精品香港三级国产av潘金莲 | 久久久久精品久久久久真实原创| 亚洲精品成人av观看孕妇| 国产免费福利视频在线观看| 大片免费播放器 马上看| 精品人妻熟女毛片av久久网站| 欧美少妇被猛烈插入视频| 国产一区有黄有色的免费视频| 亚洲欧美成人综合另类久久久| 亚洲精品在线美女| 日韩av在线免费看完整版不卡| 一本大道久久a久久精品| videosex国产| 久久青草综合色| 宅男免费午夜| 国产精品 欧美亚洲| 国产又爽黄色视频| 99久久精品国产亚洲精品| 18禁观看日本| 波多野结衣一区麻豆| 九色亚洲精品在线播放| 男女下面插进去视频免费观看| 午夜福利影视在线免费观看| 久久久国产精品麻豆| 我的亚洲天堂| 亚洲第一青青草原| 免费av中文字幕在线| 久久国产精品男人的天堂亚洲| 中国三级夫妇交换| 国产亚洲精品第一综合不卡| 亚洲国产av新网站| 18禁动态无遮挡网站| 只有这里有精品99| 亚洲欧美日韩另类电影网站| videosex国产| 黄色怎么调成土黄色| 欧美黑人欧美精品刺激| av天堂久久9| av视频免费观看在线观看| 自拍欧美九色日韩亚洲蝌蚪91| 国产日韩欧美亚洲二区| 99久久精品国产亚洲精品| 日韩制服丝袜自拍偷拍| 99香蕉大伊视频| 老汉色∧v一级毛片| 久久99精品国语久久久| 777久久人妻少妇嫩草av网站| 久久人妻熟女aⅴ| 最近手机中文字幕大全| 你懂的网址亚洲精品在线观看| 毛片一级片免费看久久久久| 亚洲精品美女久久av网站| 激情五月婷婷亚洲| 午夜福利乱码中文字幕| 精品午夜福利在线看| 国产精品久久久av美女十八| 女人精品久久久久毛片| 亚洲少妇的诱惑av| 日本vs欧美在线观看视频| 嫩草影视91久久| 视频区图区小说| 欧美 日韩 精品 国产| 国产精品一国产av| 老汉色∧v一级毛片| 街头女战士在线观看网站| 久久人人爽人人片av| 亚洲av中文av极速乱| 水蜜桃什么品种好| 日韩一本色道免费dvd| 最近的中文字幕免费完整| 亚洲av中文av极速乱| 国产乱来视频区| 欧美精品一区二区免费开放| 国产成人欧美| 欧美日韩福利视频一区二区| 男人舔女人的私密视频| 精品一区二区三区四区五区乱码 | 免费观看性生交大片5| 黄色一级大片看看| 高清不卡的av网站| 亚洲成色77777| 亚洲欧美一区二区三区久久| 精品国产露脸久久av麻豆| 老司机影院成人| 精品福利永久在线观看| 欧美成人午夜精品| 亚洲美女黄色视频免费看| 亚洲国产欧美日韩在线播放| 免费在线观看黄色视频的| 亚洲精品一区蜜桃| 十分钟在线观看高清视频www| 免费黄频网站在线观看国产| 日韩中文字幕视频在线看片| 久久狼人影院| 男女国产视频网站| 欧美黄色片欧美黄色片| xxxhd国产人妻xxx| 国产成人精品在线电影| 午夜福利影视在线免费观看| 制服丝袜香蕉在线| 水蜜桃什么品种好| 国产精品国产三级专区第一集| 久久精品久久久久久久性| 波多野结衣一区麻豆|