Improvement of visibility of moiré fringe in X-ray differential phase-contrast imaging

To fabricate high performance Bi absorption gratings for use in X-ray differential phase-contrast imaging (DPCI), the micro-casting method was improved via surface modification. Bi2O3was used in place of SiO2as an improved wetting layer. A scanning electron microscopy showed that a high filling-ratio analyzer grating with a period of 3 μm and a depth of 150 μm was obtained. Furthermore, the superiority of the presented analyzer grating to the one fabricated using the traditional micro-casting method was revealed through a comparison of moiré patterns. These tests demonstrate an enhancement to the micro-casting method for the fabrication of absorption gratings.

optical engineering; X-ray; phase contrast; absorption grating; micro-casting; moiré fringe; bismuth

X射線微分相襯成像系統(tǒng)莫爾條紋對比度的改善

深圳大學光電工程學院，光電子器件與系統(tǒng)教育部/廣東省重點實驗室，廣東深圳 518060

Since Pfeiffer et al.[1]proposed the use of an X-ray tube in X-ray differential phase-contrast imaging (DPCI), the technology has garnered more attention than other X-ray phase-contrast methods. As a result, DPCI is expected to find applications in product inspection, medical imaging, and other non-destructive observation systems[2-5].

The quality of a phase-contrast image depends strongly on the visibility of the moiré fringe[6-7]. The main factor influencing the fringe visibility is the transmission of X-ray through the absorption grating metal[8]. For the device presented in this work, the transmission is determined primarily by the height of Bi in the absorption grating[9]. This paper reports an improvement to the micro-casting process, which is used to fabricate an analyzer grating with a higher Bi filling-ratio to enhance moiré fringe visibility. Differing from LIGA (lithography, electroplating and molding) and David’s process[10-13], the micro-casting method has proven to be a low-cost way to fabricate Bi absorption gratings[14]. The fabrication process as previously described involves the formation of high aspect-ratio (HAR) grating structures, surface modification, and the filling of these structures with molten Bi[15]. However, in previous efforts, the molten Bi did not fully fill these structures (period of 3 μm and depth of 150 μm), especially close to the bottom. It was concluded that insufficient wettability between the layer of the SiO2and the molten Bi might have been the issue. To address this issue, Bi(NO3)3in acetone was used to fill the grating structures and to cover the side walls under vacuum pressure and ultrasonic treatment. Bi(NO3)3then decomposed to Bi2O3before the molten Bi filling to avoid the agglomerate of unwanted Bi on the upper surface of the analyzer grating. Furthermore, to quantify the improved performance of the presented analyzer grating in comparison to the previously produced one, a comparison between their moiré fringes is given.

1　Experiment

Fig.1　Scanning electron microscope(SEM) image of the upper surface of the analyzer grating圖1　分析光柵結(jié)構(gòu)上表面的電鏡照片

For the first step of micro-casting, the analyzer grating structure was fabricated using photo-assisted electrochemical etching (PAEE)[16-17]. A structure was obtained with a period of 3 μm and a depth of 150 μm in a 5-inch n-type <100> silicon wafer. This process has been reported previously[15,18]. Note that the side walls of the analyzer grating were reinforced by the vertical walls, giving the analyzer grating the appearance of a pore array, as shown in Fig.1.

In the second step, a wetting layer was established on the surfaces, including the side walls. The improved surface modification can be divided into two stages: filling with low and high concentration solutions; and the transformation from Bi(NO3)3to Bi2O3. First, Bi(NO3)3was dissolved in highly volatile acetone to form low (4%) and high (29%) concentration solutions. Experiments revealed that different concentration Bi(NO3)3solutions showed different physical characteristics on the structure surfaces. A lower concentration solution results in a smaller contact angle, which is beneficial to overcoming surface tension. Therefore, after the structure was filled with the low concentration solution, a thin Bi(NO3)3layer was deposited on the surface of side walls. A higher concentration solution results in a larger contact angle, which can make it difficult (or impossible) to enable complete filling. However, a small contact angle would appear if the high concentration solution contacts with the thin layer formed by the low concentration solution. As a result, more Bi(NO3)3was introduced. Therefore, successive application of the low and the high concentration solutions in a vacuum environment ensured full application of the Bi(NO3)3along all surfaces. It should be noted that the solution flowed freely into the structures if sonicated at a frequency of 80 kHz. The Bi(NO3)3collects unwanted Bi agglomerates on the upper surface of the analyzer grating after the third step, but the Bi2O3leads to a clean surface. Therefore, for the second stage, after the solvent was completely dispersed, the structure was heated to 600 ℃ to transform the Bi(NO3)3·5H2O in the structure to a Bi2O3powder.

For the third step, the analyzer grating structure was filled with molten Bi by use of a high temperature and pressure furnace, which has been described previously[15]. The structure was immersed into the container, which is full of molten Bi. Due to the wetting layer and the applied pressure (0.7 MPa), the molten Bi flowed freely into the HAR structure until it reached the bottom. Then, the structure was removed from the container and allowed to cool to room temperature.

2　Results and test

A SEM cross-section back-scattered image of the analyzer grating is shown in Fig.2. The bright lines correspond to the filled Bi. It should be noted that during the preparation of the sample, breakage can occur in a filled Bi line, as shown in the black outlines in Fig.2. The interruptions of some Bi lines result in the observation of some dark regions. The result shows that the molten Bi reached the bottom of the grating structure. Compared to existing results[14], the advantage of the improved micro-casting method is clear. Additionally, a source grating was also fabricated using the improved micro-casting method, and the SEM cross-section image is shown in Fig.3. The black and the grey regions correspond to the silicon and the filled Bi, respectively.

Fig.2　SEM cross-section back-scattered image of the analyzer grating圖2　分析光柵側(cè)視電鏡背散射照片

To evaluate performance, an X-ray DPCI system was constructed to observe the improvement of the analyzer gratings from the contrast of moiré fringes. Two absorption gratings (a source grating with period of 42 μm and depth of 150 μm and an analyzer grating) and a phase grating (period of 5.6 μm and depth of 41 μm) were used, as shown in Fig.4. The distance between the source grating and the phase grating was 1 470 cm, and the distance between the phase grating and the analyzer grating was 10.5 cm. The conventional tungsten target X-ray tube was run at 60 kV/ 2 mA. A CsI(Tl) scintillator is coupled to a cooled CCD camera (ANDOR 2 048×2 048, 13.5 μm/pixel) through a fiber tape with a magnification of 0.5 as the image detector. Through adjustment of the angle between the phase grating and the analyzer grating, the moiré fringes were registered by the detector, as shown in Fig.5(a). The moiré fringe pattern shown in Fig.5(b) corresponds to the analyzer grating fabricated using the previous micro-casting method. The normalized intensities along the lines in Fig.5(a) and Fig.5(b) are shown in Fig.5(c) and Fig.5(d). From this measurement, the improvement percentage of the fringe visibility was determined to be 31.6 %.

Fig.4　Schematic diagram of the constructed DPCI system and the moiré fringe registered by the X-ray detector圖4　X射線微分相襯成像系統(tǒng)與莫爾條紋示意圖

Fig.5　Moiré fringes obtained using the DPCI system and the normalized intensities along the lines圖5　實驗獲取的X射線微分相襯成像系統(tǒng)莫爾條紋及其對應的歸一化強度曲線

Conclusions

An improved micro-casting method for the fabrication of absorption gratings was developed. The micro-casting process was improved through surface modification. By covering the grating structure with a layer of Bi2O3, the molten Bi could flow freely into the HAR microstructures, resulting in a higher filling ratio. The comparison of the visibility of moiré fringes in DPCI demonstrates that the improved micro-casting method can provide the Bi analyzer gratings with enhanced performances.

Acknowledgments：We thank Mrs. Xu Guiwen in College of Optoelectronic Engineering, Shenzhen University, for her help of the SEM images.

/

[1] Pfeiffer F, Weitkamp T, Bunk O, et al. Phase retrieval and differential phase-contrast imaging with low-brilliance X-ray sources[J]. Nature Physics, 2006, 2(4): 258-261.

[2] Momose A, Kuwabara H, Yashiro W. X-ray phase imaging using Lau effect[J]. Applied Physics Express, 2011, 4(6): 066603.

[3] Donath T, Pfeiffer F, Bunk O, et al. Phase-contrast imaging and tomography at 60 keV using a conventional X-ray tube source[J]. Review of Scientific Instruments, 2009, 80(5): 053701.

[4] Bech M, Jensen T H, Feidenhans’l R, et al. Soft-tissue phase-contrast tomography with an X-tube source[J]. Physics in Medicine and Biology, 2009, 54(9): 2747-2753.

[5] Pfeiffer F, Bech M, Bunk O, et al. Hard-X-ray dark-field imaging using a grating interferometer[J]. Nature Materials, 2008, 7(2): 134-137.

[6] Yashiro W, Takeda Y, Momose A. Efficiency of capturing a phase image using cone-beam X-ray Talbot interferometry[J]. Journal of the Optical Society of America A, 2008, 25(8): 2025-2039.

[7] Revol V, Kottler C, Kaufmann R, et al. Noise analysis of grating-based X-ray differential phase contrast imaging[J]. Review of Scientific Instruments, 2010, 81(7): 073709.

[8] Huang Jianheng, Du Yang, Lei Yaohu, et al. Noise analysis of hard X-ray differential phase contrast imaging[J]. Acta Physica Sinica, 2014, 63(16): 168702.(in Chinese)

黃建衡，杜楊，雷耀虎，等．硬X射線微分相襯成像的噪聲特性分析[J]．物理學報，2014, 63(16): 168702.

[9] Huang Jianheng, Lei Yaohu, Du Yang, et al. Quantitative analysis of fringe visibility in grating-based X-ray phase-contrast imaging[J]. Journal of the Optical Society of America A, 2016, 33(1): 69-73.

[10] Kenntner J, Grund T, Matthis B, et al. Front and backside structuring of grating for phase contrast imaging with X-ray tubes[C]// International Conference on Developments in X-ray Tomography. San Diego, USA: SPIE, 2010: 780408.

[11] Noda D, Tanaka M, Shimada K, et al. Fabrication of large area diffraction grating using LIGA process[J]. Microsystem Technologies, 2008, 14(9/10/11): 1311-1315.

[12] Noda D, Tsujii H, Takahashi N, et al. Fabrication of high precision X-ray mask for X-ray grating of X-ray Talbot interferometer[J]. Microsystem Technologies, 2010, 16(8): 1309-1313.

[13] David C, Bruder J, Rohbeck T, et al. Fabrication of diffraction gratings for hard X-ray phase contrast imaging[J]. Microelectronic Engineering, 2007, 84(5/6/7/8): 1172-1177.

[14] Lei Yaohu, Du Yang, Li Ji, et al. Application of Bi absorption gratings in grating-based X-ray phase contrast imaging[J]. Applied Physics Express, 2013, 6(11): 117301.

[15] Lei Yaohu, Du Yang, Li Ji, et al. Fabrication of X-ray absorption gratings via micro-casting for grating-based phase contrast imaging[J]. Journal of Micromechanics and Microengineering, 2014, 24(1): 015007.

[16] Lehmann V, F?ll H. Formation mechanism and properties of electrochemically etched trenches in n-type silicon[J]. Journal of The Electrochemical Society, 1990, 137(2): 653-659.

[17] Lehmann V. The physics of macropore formation in low doped n-type silicon[J]. Journal of the Electrochemical Society, 1993, 140(10): 2836-2843.

[18] Lei Yaohu, Liu Xin, Guo Jinchuan, et al. Development of X-ray scintillator functioning also as an analyser grating used in grating-based X-ray differential phase contrast imaging[J]. Chinese Physics B, 2011, 20(4): 042901.

【中文責編：方圓；英文責編：木南】

Lei Yaohu，Huang Jianheng, Liu Xin，et al．Improvement of visibility of moiré fringe in X-ray differential phase-contrast imaging[J]. Journal of Shenzhen University Science and Engineering, 2016, 33(5): 506-510.

College of Optoelectronic Engineering, Key Laboratory of Optoelectronic Devices and Systems of Ministry of Education and Guangdong Province, Shenzhen University, Shenzhen 518060, Guangdong Province, P.R.China

為制作高質(zhì)量的鉍吸收光柵以提高X射線微分相襯成像系統(tǒng)性能，針對表面改性環(huán)節(jié)對微鑄造技術(shù)進行改進,以Bi2O3取代SiO2作為改進的浸潤層．在周期為3 μm、深度為150 μm的分析光柵結(jié)構(gòu)上制作了具有高填充率的分析光柵，獲得了該光柵的掃描電子顯微鏡照片．為進一步表明改進微鑄造技術(shù)制作分析光柵的優(yōu)越性，與改進前的分析光柵進行對比．將兩種光柵先后置于X射線微分干涉相襯成像系統(tǒng)中，分別獲取了系統(tǒng)莫爾條紋．從最終的條紋對比度上判斷，改進后的微鑄造技術(shù)制作的分析光柵填充率明顯提高．

光學工程；X射線；相襯；吸收光柵；微鑄造；莫爾條紋；鉍

國家重大科研儀器設備研制專項基金資助項目(61227802)；國家自然科學基金資助項目(61405120)

雷耀虎(1984—)，男，深圳大學講師、博士．研究方向：X射線相襯成像、微納制作．E-mail: yfyt10@163.com

2016-03-07；Accepted：2016-04-05

O 434.19; O 647.5Document code: Adoi：10.3724/SP.J.1249.2016.05506

Foundation：National Special Foundation of China for Major Science Instrument (61227802); National Natural Science Foundation of China (61405120)

? Corresponding author：Associate professor Li Ji.E-mail: liji@szu.edu.cn

引文：雷耀虎，黃建衡，劉鑫，等．X射線微分相襯成像系統(tǒng)莫爾條紋對比度的改善[J]. 深圳大學學報理工版，2016，33(5)：506-510.(英文版)